Structural and magnetic properties of yttrium iron garnet (YIG) and 4 yttrium aluminum iron garnet (YAlG) nanoferrite via sol-gel synthesis


Citation

Musa, Makiyyu Abdullahi and Azis, Raba'ah Syahidah and Osman, Nurul Huda and Hassan, Jumiah and Zangina, Tasiu (2017) Structural and magnetic properties of yttrium iron garnet (YIG) and 4 yttrium aluminum iron garnet (YAlG) nanoferrite via sol-gel synthesis. Results in Physics, 7. 1135 - 1142. ISSN 2211-3797

Abstract

The structural and magnetic properties of yttrium iron garnet (YIG) and yttrium aluminum iron garnet (Y3AlxFe5−xO12, YAIG) (x = 0.2, 0.6, 1, 1.4, 1.8, and 2.2) nanoparticles were investigated. The samples were prepared via auto combustion sol-gel technique, using citric acid as chelating agent and fuel for the combustion process. The obtained powder was heated at 950 °C. X-ray diffraction peaks confirmed the garnet phase formation. Crystallite size increases with Al from 28.5894 to 28.6170 nm. Lattice constant of the samples was found to decrease from 12.4674 Å to 12.3233 Å as Al increase from 0.0 to 2.2. FTIR was used to confirm the garnet structure, the main vibrating modes were observed to shift to higher wave number with increasing Al concentration. Saturation magnetization, Ms shows a decreasing trend from 20.721 to 0.7586 emu/g with increasing Al from 0.0 to 2.2. Furthermore, the decreasing trends in the static magnetic properties of YAIG samples may be due to the introduction of Al ions in the YIG crystal lattice. High content of Al substitution on YIG leads to paramagnetic behavior of the ferrite. The grain size decreased from 0.64 μm to 0.32 μm, while the bulk density decreased from 5.058 gcm−3 to 4.233 gcm−3 as Al increase from 0.0 to 2.2.


Download File

[img] Text
Structural and magnetic properties of yttrium iron garnet (YIG) and yttrium aluminum iron garnet (YAlG) nanoferrite via sol-gel synthesis.pdf
Restricted to Repository staff only

Download (1MB)

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
DOI Number: https://doi.org/10.1016/j.rinp.2017.02.038
Publisher: Elsevier
Keywords: YIG; YAIG; Sol-gel; Phase composition; Magnetic properties
Depositing User: Mohd Hafiz Che Mahasan
Date Deposited: 15 Oct 2018 03:01
Last Modified: 15 Oct 2018 03:01
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.1016/j.rinp.2017.02.038
URI: http://psasir.upm.edu.my/id/eprint/63302
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item