Observation of cotton-like bismuth oxide (β-Bi2O2.5) prepared via pulsed laser ablation deposition

Monoclinic bismuth oxide (α-Bi2O3) nanoparticles were prepared via precipitation method and irradiated with a pulsed laser forming thin films. Their phase and surface morphological properties were investigated using x-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HR-TEM). The XRD analysis shows the phase transformation to a partially crystalline tetragonal phase β-Bi2O3 thin film. The SEM micrograph of the nanoparticles, with an average crystal size of 72 nm, was seen to form a thin film with a peculiar structure, coined as “cotton-likeâ€�, is attributed to the high surface energy absorbed by the nanoparticles during ablation. The HR-TEM micrograph shows the particulate with a clearly defined interlayer spacing.

Preview PDF Observation of Cotton-like Bismuth Oxide (β-Bi2O2.5) Prepared via Pulsed Laser Ablation Deposition.pdf Download (2MB) | Preview Official URL or Download Paper: http://www.pertanika.upm.edu.my/Pertanika%20PAPERS...

Actions (login required)

View Item