Effects of PVA-PEG binders system on microstructure and properties of sintered alumina


Citation

Jaafar, Che Nor Aiza and Zainol, Ismail and Sulaiman, Shamsuddin and Ayub, M. Ikhwan (2014) Effects of PVA-PEG binders system on microstructure and properties of sintered alumina. Applied Mechanics and Materials, 564. pp. 355-360. ISSN 1660-9336; ESSN: 1662-7482

Abstract

In this work, the effects of binder compositions on the mechanical properties, density, volume shrinkage and microstructure of sintered alumina were investigated. Three different formulations of alumina samples were prepared by mixing alumina with 3 % of poly (ethylene glycol) (PEG) with 1 to 3 wt% of poly (vinyl alcohol) (PVA) binders. The degradation temperature of binder was investigated by means of thermogravimetry analysis (TGA). Diametral compressive test was conducted to determine the tensile strength of sintered alumina. Scanning electron microscopy (SEM) was used to characterise the microstructure and fracture surface analysis. It was found that PVA binder plays important roles in sintering of alumina. The relative density and tensile strength increase as the percentages of PVA increase for each sintering temperature but the volume shrinkages are not much affected by binder composition. The results inferred that alumina samples which have 3%wtPVA-3%wtPEG binder sintered at 1600 °C shows the highest tensile strength (129 MPa) compared to other formulations.


Download File

[img]
Preview
PDF (Abstract)
Effects of PVA.pdf

Download (85kB) | Preview
Official URL or Download Paper: http://www.scientific.net/AMM.564.355

Additional Metadata

Item Type: Article
Divisions: Faculty of Engineering
DOI Number: https://doi.org/10.4028/www.scientific.net/AMM.564.355
Publisher: Trans Tech Publications
Keywords: Alumina; Binder; Polyethylene glycol (PEG); Polyvinyl alcohol (PVA)
Depositing User: Nabilah Mustapa
Date Deposited: 23 May 2015 11:02
Last Modified: 05 Oct 2015 01:13
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.4028/www.scientific.net/AMM.564.355
URI: http://psasir.upm.edu.my/id/eprint/37384
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item