Synthesis and properties of zinc-aluminium-acetylsalicylate-nanocomposite


Citation

Yahaya, Asmah and Hussein, Mohd Zobir and Zainal, Zulkarnain and Mamat, Mazidah (2005) Synthesis and properties of zinc-aluminium-acetylsalicylate-nanocomposite. In: International Advanced Technology Congress: Conference on Advanced Materials (CAM 2005), 6-8 Dec. 2005, Putrajaya, Malaysia. (pp. 331-339).

Abstract

Intercalation of acetylsalicylate anion into zinc-aluminium-layered double hydroxide has been successfully accomplished via co-precipitation method. Good crystallinity of both the zinc-aluminium-layered double hydroxide (ZANO) and the zinc-aluminium-acetylsalicylate-nanocomposite (ZAAS) were obtained when the Zn/Al ratio used was 3. Expansion of the basal spacing of the layered double hydroxide (LDH) after intercalation process from 8.9 Å to 16.3 Å was observed. However, FTIR analysis showed that nitrate anion was co-intercalated into the interlayer of the nanocomposite and the result was in agreement with the elemental analysis. TGA-DTG results showed that the encapsulation of the acetylsalicylate anion into the interlayer increased its thermal stability. The nitrogen adsorption-desorption isotherms showed that the resulting materials were of Type IV with H3 hysteresis loop. SEM micrograph of ZANO showed its flaky-like structure; while that of ZAAS showed a compact structure.


Download File

[img] PDF (Full text)
33860.pdf - Published Version
Restricted to Repository staff only

Download (277kB)

Additional Metadata

Item Type: Conference or Workshop Item (Poster)
Divisions: Faculty of Science
Institute of Advanced Technology
Publisher: Universiti Putra Malaysia Press
Keywords: Zinc; Aluminium; Acetylsalicylate; Nanocomposite
Depositing User: Erni Suraya Abdul Aziz
Date Deposited: 28 Apr 2015 08:50
Last Modified: 25 Sep 2018 01:52
URI: http://psasir.upm.edu.my/id/eprint/33860
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item