Nanocrystallization of CK60 commercial steel by drilling method


Citation

Nosrati, Shohreh and Mohd Tahir, Suraya and Mohamed Ariff, Azmah Hanim and Hashim, Mansor (2011) Nanocrystallization of CK60 commercial steel by drilling method. Australian Journal of Basic and Applied Sciences, 5 (8). pp. 1224-1228. ISSN 1991-8178

Abstract

Drilling as a novel Surface Sever Plastic Deformation method (SSPD) has been applied to commercial CK60 steel plate to create a Nano Crystalline (NC) structured layer. In present study, the CK60 steel plate has been quenched in room temperature water from 950 °C (1 Hr) and tempered in 350°C for one hour. Drilling has been done with use of Ti-Carbide coated drilling bit under 10, 15 and 20 m/min speeds. The microstructure of the samples was studied by light microscope and high resolution SEM. The formation of NC layer having grain size in the order of 50nm was confirmed by the SEM observation and applying Hall-Pitch formula on the samples drilled with 15 m/min speed. The created fine grain zone is separated from base metal structure and clear boundary with 1 to 10 microns thickness where the drilling speed changes from 15 to 20 m/min. The microhardness test result illustrates that the hardness of surface NC layer increases almost more than twice when compared with coarse grain structure of base metal.


Download File

[img]
Preview
PDF (Abstract)
Nanocrystallization of CK60 commercial steel by drilling method.pdf

Download (83kB) | Preview
Official URL or Download Paper: http://www.ajbasweb.com/old/ajbas_August_2011.html

Additional Metadata

Item Type: Article
Divisions: Faculty of Engineering
Institute of Advanced Technology
Publisher: American-Eurasian Network for Scientific Information
Keywords: Nano crystallinization; SSPD; Drilling; CK60 steel
Depositing User: Muizzudin Kaspol
Date Deposited: 04 Nov 2014 07:20
Last Modified: 24 Sep 2018 07:47
URI: http://psasir.upm.edu.my/id/eprint/23242
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item