Preparation and physical properties of polypyrrole / zeolite composites

Polypyrrole (PPy′)/zeolite composites were synthesized via chemical oxidation of pyrrole in the presence of zeolite. FeCl3 was used as an oxidant with the FeCl3-to-pyrrole molar ratio (MR) equal to 1. The zeolite contents were 0%, 5%, 10%, 15% and 20% of the total weight of PPy′. For comparison, pure PPy″ with FeCl3–pyrrole MR equal to 2 was also synthesized using the same method. The structural and physical properties of the samples were studied using X-rays diffraction (XRD), Fourier transform infrared spectroscopy, field emission electron scanning microscopy, thermogravimetric analysis, van Der Pauw technique and UV–VIS-NIR spectroscopy. The XRD of PPy′/zeolite (5%) revealed a presence of crystalline nature of zeolite in a spectrum of host amorphous PPy′. The XRD peaks increased, became stronger and shifted slightly to higher 2θ in PPy′/zeolite (10–20%) composites. Compared with PPy′, the composites were denser, more compact and had better thermal stability. The composites conductivity increased while their bandgap tended to reduce with increasing of zeolite. PPy′/zeolite (20%) composite had the highest conductivity value of 3.6 S cm−1 with an optical bandgap of 2.21 eV. The results showed that zeolite has been incorporated into PPy′ matrix and improved its physical properties.

Text (Abstract) Preparation and physical properties of polypyrrole zeolite composites.pdf Download (64kB) Official URL or Download Paper: https://www.sciencedirect.com/science/article/pii/...

Actions (login required)

View Item