Sintering behaviour of cemented tungsten carbide and steel bilayer

The target of processing bimaterial components by cost effective powder metallurgy is to combine unique properties from different parts of the component. Differential shrinkage rate and more often, radial mismatch which is more consistent in bilayer owing to sintering conditions (time, rate, temperature etc.) is known to compromise the interfacial bond strength and integrity of these components. Therefore, the aim of this study is to analyze the sintering compatibility and evaluate the mismatch strain in cemented tungsten carbide (WC-Fe-C) and steel (Fe-W-C) bilayer processed through powder metallurgy (PM) to combine the hardness and toughness properties applicable in machining industries for drilling tools. Through geometrical measurement, mismatch strain rate between layers at different sintering temperatures was calculated and a value as low as 13.7% was observed at the interfacial zone of MC–0.2 specimen sintered at 1280°C indicating a stronger bond between layers compared to those sintered at 1290°C and 1295°C where a huge mismatch was found increasing the tendency for delamination.

Preview Text (Abstract) Sintering behaviour of cemented tungsten carbide and steel bilayer.pdf Download (103kB) | Preview Official URL or Download Paper: https://www.scientific.net/KEM.740.60

Actions (login required)

View Item