The variation of optical absorption edge with sintering time for the ceramic ZnO + xMnO2-Bi2O3-TiO2


Citation

Rizwan, Zahid and Zakaria, Azmi (2008) The variation of optical absorption edge with sintering time for the ceramic ZnO + xMnO2-Bi2O3-TiO2. In: 2008 IEEE International Conference on Semiconductor Electronics (ICSE 2008), 25-27 Nov. 2008, Johor Bahru, Malaysia. (pp. 541-544).

Abstract

Photopyroelectric spectroscopy is used to study the variation of optical absorption of the ceramic xMn02 - 0.4 Bi2O3 - 0.4 TiO2 - ZnO, x = 0, 0.4 mol% sintered for 1-4 hours at the isothermal temperature, 1220°C. The wavelength of incident light, modulated at 12 Hz, is kept in the range 310 to 810 nm. The band-gap energy is reduced from 3.2 eV (for pure ZnO) to 2.83 eV for 0 mol% MnO2 for 1 hour sintering time and decreases further with the further increase of sintering time. Eg is decreased to 2.39 eV for 1 hour sintering time after the addition of 0.4 mol% of MnO2 in the ceramic combination. It is reduced to a value 1.9 eV with the further increase of sintering time. The variation of steepness factor σA and σB which characterizes the slop of exponential optical absorption, is correlated with the variation of Eg, sintering time and doping of MnO2. Microstructure and compositional analysis of the selected areas are analyzed using SEM and EDAX.


Download File

[img] Text (Abstract)
The variation of optical absorption edge with sintering time for the ceramic ZnO + xMnO2-Bi2O3-TiO2.pdf

Download (50kB)

Additional Metadata

Item Type: Conference or Workshop Item (Paper)
Divisions: Faculty of Science
DOI Number: https://doi.org/10.1109/SMELEC.2008.4770383
Publisher: IEEE
Keywords: Photopyroelectric spectroscopy; Optical absorption
Depositing User: Nabilah Mustapa
Date Deposited: 10 Aug 2020 02:23
Last Modified: 10 Aug 2020 02:23
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.1109/SMELEC.2008.4770383
URI: http://psasir.upm.edu.my/id/eprint/37569
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item