Characterization of mechanical and microstructural properties of palm oil fuel ash geopolymer cement paste


Citation

Salih, Moslih Amer and Abang Ali, Abang Abdullah and Farzadnia, Nima (2014) Characterization of mechanical and microstructural properties of palm oil fuel ash geopolymer cement paste. Construction and Building Materials, 65. pp. 592-603. ISSN 0950-0618

Abstract

This study delineates activation of palm oil fuel ash (POFA) by a combination of sodium silicate and sodium hydroxide at 60 °C to be used as a geopolymer binder. Qualitative observations as well as compressive strength were recorded to assess the viability of POFA utilization. Also, XRD, SEM/EDX, DSC, FTIR tests were conducted to investigate underlying mechanisms of geopolymerization. The post-test observations revealed that activation of POFA is applicable and compressive strength of up to 32.48 MPa at the age of 28 days was achieved. Chemical tests indicated that formation of calcium silicate hydrate was the dominant cause of geopolymerization.


Download File

[img]
Preview
PDF (Abstract)
Characterization of mechanical and microstructural properties of palm oil fuel ash geopolymer cement paste.pdf

Download (83kB) | Preview

Additional Metadata

Item Type: Article
Divisions: Faculty of Engineering
DOI Number: https://doi.org/10.1016/j.conbuildmat.2014.05.031
Publisher: Elsevier
Keywords: Palm oil fuel ash; POFA; Alkali activation; Geopolymer binder
Depositing User: Nabilah Mustapa
Date Deposited: 20 May 2015 12:07
Last Modified: 26 Jan 2016 01:00
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.1016/j.conbuildmat.2014.05.031
URI: http://psasir.upm.edu.my/id/eprint/36759
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item