Microhardness characteristics of AL-6063 alloy processed by equal channel angular extrusion


Citation

Nemati, Jamshid and Sulaiman, Shamsuddin and Baharudin, B. T. Hang Tuah and Mohamed Ariff, Azmah Hanim and Majzoobi, Gholam Hossein (2014) Microhardness characteristics of AL-6063 alloy processed by equal channel angular extrusion. Applied Mechanics and Materials, 564. pp. 513-518. ISSN 1660-9336; ESSN: 1662-7482

Abstract

In this study, annealed AL-6063 alloy was processed by the Equal Channel Angular Extrusion (ECAE) up to 6 passes at a temperature of 200°c following route A with a constant ram speed of 30 mm/min through a die angle of 90° between the die channels. The influence of ECAE processing on the evolution of microhardness in the material was studied using Vickers microhardness testing. The detailed analysis was carried out on the samples of as-received, one, two, three, four, five, and six pass conditions. The grain diameter reduced from 45μm to 2.8 μm after 6 passes of ECAE. The results indicated around 90% increase in Microhardness after 5 passes. Hardness of the inner surface where the billet was under compression was slightly higher than that of the mid-surface.


Download File

[img]
Preview
PDF (Abstract)
Microhardness characteristics of AL-6063 alloy processed by equal channel angular extrusion.pdf

Download (50kB) | Preview
Official URL or Download Paper: http://www.scientific.net/AMM.564.513

Additional Metadata

Item Type: Article
Divisions: Faculty of Engineering
DOI Number: https://doi.org/10.4028/www.scientific.net/AMM.564.513
Publisher: Trans Tech Publications
Keywords: AL-6063; Equal channel angular extrusion; Grain size; Vickers microhardness
Depositing User: Nurul Ainie Mokhtar
Date Deposited: 19 Sep 2016 02:22
Last Modified: 19 Sep 2016 02:22
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.4028/www.scientific.net/AMM.564.513
URI: http://psasir.upm.edu.my/id/eprint/34514
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item