Influence of Pt doping on the sensing mechanism of La2O3/SnO2 thick film for CO2 gas


Ehsani, Maryam and Hamidon, Mohd Nizar (2014) Influence of Pt doping on the sensing mechanism of La2O3/SnO2 thick film for CO2 gas. International Journal of Applied Electronics in Physics and Robotics, 2 (1). pp. 6-7. ISSN 2203-0069


Thick film CO2 sensors were fabricated using La2O3/SnO2 loaded with Pt and in the unloaded form. The nano-crystalline powders of SnO2-La2O3-Pt synthesized by high speed ball milling method were screen-printed on alumina substrates. The resistance of fabricated sensors were measured against different CO2 concentration in the working temperature of 225 C. The composition that gives an acceptable resistivity for CO2 was in the 3wt.% ratio of Pt.

Download File

[img] PDF
Influence of Pt Doping on the Sensing Mechanism of.pdf
Restricted to Repository staff only

Download (495kB)

Additional Metadata

Item Type: Article
Divisions: Faculty of Engineering
Institute of Advanced Technology
DOI Number: https://doi.org/10.7575/aiac.ijaepr.v.2n.1p.6
Publisher: Australian International Academic Centre
Keywords: CO2 gas; Thick film gas sensors; La2O3/ SnO2; Screen printing method; Pt.
Depositing User: Nurul Ainie Mokhtar
Date Deposited: 09 Dec 2015 02:14
Last Modified: 09 Dec 2015 02:14
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.7575/aiac.ijaepr.v.2n.1p.6
URI: http://psasir.upm.edu.my/id/eprint/34202
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item