Synthesis and impedance studies of CuTa2-2xO6-5x perovskites


Citation

Chon, Mun Ping and Tan, Kar Ban and Khaw, Chwin Chieh and Zainal, Zulkarnain and Yap, Taufiq Yun Hin (2013) Synthesis and impedance studies of CuTa2-2xO6-5x perovskites. Advanced Science Letters, 19 (3). pp. 992-996. ISSN 1936-6612; ESSN: 1936-7317

Abstract

Polycrystalline samples of CuTa2-2xO6-5x are successfully synthesised by solid state reaction at 975 °C over 24 hours and the solid solution limit is confirmed as 0 1 ≤ x ≤ 0 2. The samples are fully indexed based on cubic structure in the space group, Pmmm, International Centre for Diffraction data (ICDD) number 70-611. The refined lattice parameters for CuTa1.8O5.5 (x = 0 1) and CuTa1.6O5 (x = 0 2) are a = 7 5117 (4) and 7.5070 (16), respectively. The determined grain sizes for both samples are in the range of 0.5-3.0 μm for x = 0 1 and 1.0-4.0 μm for x = 0 2. Besides, the samples show no thermal change in a wide range of temperature studied. Meanwhile, high relative permittivity exhibited by sample x = 0 2 at room temperature is also accompanied with high dielectric loss. The recorded activation energies, Ea are relatively low ~ 0.28-0.33 eV and high conductivity in higher copper content sample. i.e., x=0.2 is probably attributed to the conductive behavior of copper.


Download File

[img]
Preview
PDF (Abstract)
Synthesis and impedance studies of CuTa2.pdf

Download (186kB) | Preview

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
DOI Number: https://doi.org/10.1166/asl.2013.4865
Publisher: American Scientific Publishers
Keywords: Electrical properties; Perovskite; Solid state method; X-ray diffraction
Depositing User: Umikalthom Abdullah
Date Deposited: 10 Sep 2014 03:11
Last Modified: 28 Nov 2016 03:45
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.1166/asl.2013.4865
URI: http://psasir.upm.edu.my/id/eprint/30178
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item