Dielectric properties of La0.67sr0.33Mnl-xTix03 with x = 0.4 and 0.6.


Citation

Zalita , Z. and Shaari, Abdul Halim and Wan Yusoff, Wan Mohamad Daud and Lim, Kean Pah and Talib , Zainal Abidin and Mazni, M. (2011) Dielectric properties of La0.67sr0.33Mnl-xTix03 with x = 0.4 and 0.6. Solid State Science and Technology, 19 (1). pp. 169-174. ISSN 0128-7389

Abstract

The dielectric properties of Ti-substituted La0.67Sr0.33Mn1-xTixO3 with x = 0.4 and 0.6 as a function of frequency and temperature have been investigated. The samples have been prepared using the conventional solid state reaction method at 1300oC. Both samples showed rhombohedral structure with R3C space group. The grain size of x = 0.4 and 0.6 are ~2.5 to 3.3 μm and ~0.4 to 0.9 μm respectively. The dielectric constant, ε' of the samples decreases with frequency but increases with temperature. We have successfully obtained very high dielectric constant material. The highest ε' value for LSMT with x = 0.4 and 0.6 are at frequency of 10 Hz and temperature 300 K, which are ~5.7 x 106 and ~2.4 x 106. The tan δ increases with temperature for x = 0.6 but shows a peak at a certain temperature for x = 0.4. Sample with x = 0.4 has better dielectric properties compared to x = 0.6 sample because it has higher ε' and lower tan δ value. At 175 K and 1 kHz sample with x = 0.4 shows the best dielectric properties with a high ε’ value and low tan δ which are 1.1 x 105 and 0.8 respectively.


Download File

[img]
Preview
PDF (Abstract)
Dielectric properties of La0.67sr0.33Mnl-xTix03 with x = 0.4 and 0.6..pdf

Download (152kB) | Preview
Official URL: http://www.ukm.my/mass/

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
Publisher: Malaysian Solid State Science and Technology Society (MASS)
Keywords: LSMO; Dielectric properties.
Depositing User: Nur Farahin Ramli
Date Deposited: 01 Aug 2013 00:47
Last Modified: 18 Nov 2015 03:30
URI: http://psasir.upm.edu.my/id/eprint/25038
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item