Synthesis and charaterization of magnesium zinc ferrites as electromagnetic source


Citation

Yahya, Noorhana and Mohamad Nor Aripin, Ami Salwani and A. Aziz, Azizuddin and Daud, Hanita and Mohd Zaid, Hasnah and Lim, Kean Pah and Maarof, Norehan (2008) Synthesis and charaterization of magnesium zinc ferrites as electromagnetic source. American Journal of Engineering and Applied Sciences, 1 (1). pp. 53-56. ISSN 1941-7020; ESSN: 1941-7039

Abstract / Synopsis

Fabrication of Mg1-XZnXFe2O4 (where x = 0.2, 0.3, 0.4 and 0.5) samples using a conventional technique is reported. Oxides of magnesium, zinc and iron with purity of about 99.99% were mixed with distilled water in a milling machine for 12 hours. They were then filtered and presintered at 1250°C and sintered at 1350°C for 10 h in air. The phase and the crystal structure of the asprepared samples were identified using X-Ray Diffraction analysis (XRD). Hysteresis graph was evaluated using Vibrating Sample Magnetometer (VSM) to get the saturation magnetization (emu g-1)and coercivity (G) value. Atomic Force Microscope (AFM) was used to observe the surface morphology. The X-ray diffraction analysis showed major peak at plane (3 1 1) of the cubic structure for all the ferrites. The largest value of density achieved was 4.69 gcm-3 which was exhibited by sample with 0.5 mole fraction of zinc content. Highest saturation magnetization value (3.652emu g-1)was obtained for the 0.3 mole fraction of zinc content. A strong correlation between the saturation magnetization and zinc content was observed. We speculate that it is due to the Heisenberg superexchange interaction of magnetic Fe3+ and non-magnetic Zn2+ occupying the tetrahedral sites. The sample was used to induce electromagnetic (EM) waves in high operating frequency (5 MHz).


Download File

[img] PDF
ajeassp.2008.53.56.pdf
Restricted to Repository staff only

Download (184kB)

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
DOI Number: https://doi.org/10.3844/ajeassp.2008.53.56
Publisher: Science Publications
Keywords: Tetrahedron; X-ray diffraction; Hysteresis; Electromagnetic field; Super-exchange interaction
Depositing User: Najwani Amir Sariffudin
Date Deposited: 27 Aug 2012 09:20
Last Modified: 04 Dec 2017 09:55
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.3844/ajeassp.2008.53.56
URI: http://psasir.upm.edu.my/id/eprint/16938
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item