Preparation and characterization of furfuryl alcohol derived carbon coated monolith


Citation

Darmadi, and Choong, Thomas Shean Yaw and Abdullah, Luqman Chuah and Yunus, Robiah and Yap, Taufiq Yun Hin (2008) Preparation and characterization of furfuryl alcohol derived carbon coated monolith. International Journal of Science Engineering and Technology, 1 (2). pp. 41-46. ISSN 1985-3785

Abstract

This paper reports the preparation and characterization of activated carbon coated monolith. The carbons have been prepared based on furfuryl alcohol (FA) added with or without poly ethylene glycol (PEG-600) as a pore forming agent. The carbon coated monoliths are characterized by thermo-gravimetrical analysis, elemental analysis, scanning electron microscopy, and textural analysis. The carbon content of the materials is found to be about 75 wt % and the thickness of carbon coated monolith measured by scanning electron microscopy (SEM) is of ~ 38 µm. The carbon sourced from only FA exhibits adsorption Type I, whilst the carbon sourced from FA + PEG-600 is of Type IV. Brunauer, Emmett, and Teller (BET) surface areas measured by N 2 adsorption are 362.71 and 341 m 2 /g carbon , respectively. Total pore volume of the samples FA and FA + PEG-600 are 0.2 and 0.38 m 2 /g carbon, respectively.


Download File

[img]
Preview
PDF (Abstract)
Preparation and characterization of furfuryl alcohol derived carbon coated monolith.pdf

Download (85kB) | Preview

Additional Metadata

Item Type: Article
Divisions: Faculty of Engineering
Faculty of Science
Publisher: ILRAM Publisher
Keywords: Characterization; Carbon coated monolith; Furfuryl alcohol
Depositing User: Nabilah Mustapa
Date Deposited: 25 Sep 2015 02:40
Last Modified: 12 Nov 2015 07:22
URI: http://psasir.upm.edu.my/id/eprint/16309
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item