High saturation induction for Bi-substituted yttrium iron garnet prepared via sol gel technique


Citation

Yahya, Noorhana and Goh, Kah Hean (2007) High saturation induction for Bi-substituted yttrium iron garnet prepared via sol gel technique. American Journal of Applied Sciences, 4 (2). pp. 80-84. ISSN 1546-9239; ESSN: 1554-3641

Abstract / Synopsis

Y3.0-xBixFe5O12 samples (x = 0.2 and 0.4) were prepared via novel sol-gel and conventional solid-state techniques. The effect of bismuth in both techniques was investigated in terms of shrinkage,density, hysteresis and initial permeability. Sharp and clear diffraction XRD lines with highest peak appear at about 32° of the 2θ, for all the powders sintered at 900°C and 1250°C for both techniques. In evaluating the magnetic properties, it was observed that the saturation induction (1.1902kG) of sample prepared via sol-gel technique (Y2.8Bi0.2Fe5O12) is more than 200% higher than sample with the same formula prepared via conventional technique. Fine grained microstructure with average grain size of about 5μ m and higher shrinkage, about 11% were observed from the samples prepared via sol gel technique. It is concluded that samples prepared via sol gel technique appear to be an attractive route due to the possible reduction of cost of production and the enhanced magnetic and structural properties of the sample.


Download File

[img] PDF
ajassp.2007.80.84.pdf
Restricted to Repository staff only

Download (390kB)

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
Institute of Advanced Technology
DOI Number: 10.3844/ajassp.2007.80.84
Publisher: Science Publications
Keywords: Conventional solid state; Hysteresis; Initial permeability; Sol gel technique; C (conventional) S (sol-gel)
Depositing User: Najwani Amir Sariffudin
Date Deposited: 05 Aug 2010 12:49
Last Modified: 29 Nov 2017 13:05
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.3844/ajassp.2007.80.84
URI: http://psasir.upm.edu.my/id/eprint/7635
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item