Preparation and Characterization of Sr-Yig and Yig-Pva Composite

Shafie, Mohd Shamsul Ezzad (2009) Preparation and Characterization of Sr-Yig and Yig-Pva Composite. Masters thesis, Universiti Putra Malaysia.

[img] PDF
631Kb

Abstract

This thesis deals with the subject of magnetic properties utilizing iron garnet materials. The main purpose of this project is to prepare of Y3.0-XSrXFe5O12 and develop of YIG-PVA composite films. In addition, other properties including Q-factor, microstructure and XRD had also been studied. For powder preparation, seven garnet powder samples were prepared which are Y3.0- XSrXFe5O12 (x = 0 to 2.5), in the interest of 0.5 value. From the results, the highest permeability obtained at sample Y3.0Fe5O12 (YIG) which is 1.58. The lowest loss factor is 7.41, which is obtained from sample Y1.5Sr1.5Fe5O12. From the XRD characterization, the peak changing from 32.31° to 32.89°, indicating the transition from YIG to Strontium based iron garnet. From the SEM analysis, the Y2.0Sr1Fe5O12 has the largest grain size while Y3S0 exhibit smallest grain size. As a conclusion, this sample can be utilized for high frequencies applications. Considering the best microstructure, highest permeability, lower LF, the best sample is YIG. It was chosen as filler in preparation polymer composite. For polymer composite preparation, the composites consisted of polyvinyl alcohol (PVA) and YIG were prepared by casting technique. YIG (1 wt%) and YIG (5 wt%) prepared as filler in polyvinyl alcohol (PVA) as polymer composite. Both YIG exhibit similar XRD patterns to standard YIG sample including extra peak for PVA at 40°. Compared to YIG (1 wt%), the YIG (5 wt%) was more effective to improve the magnetic properties of the composites because of its network structure. In conclusion, a certain high level of filler content was proven to be necessary for the promotion of magnetic properties in oriented composite.

Item Type:Thesis (Masters)
Subject:Composite materials - Case studies
Chairman Supervisor:Associate Professor Dr. Mansor Hashim, PhD
Call Number:FS 2008 54
Faculty or Institute:Faculty of Science
ID Code:5717
Deposited By: Rosmieza Mat Jusoh
Deposited On:30 Apr 2010 02:06
Last Modified:27 May 2013 07:24

Repository Staff Only: item control page

Document Download Statistics

This item has been downloaded for since 30 Apr 2010 02:06.

View statistics for "Preparation and Characterization of Sr-Yig and Yig-Pva Composite"


Universiti Putra Malaysia Institutional Repository

Universiti Putra Malaysia Institutional Repository is an on-line digital archive that serves as a central collection and storage of scientific information and research at the Universiti Putra Malaysia.

Currently, the collections deposited in the IR consists of Master and PhD theses, Master and PhD Project Report, Journal Articles, Journal Bulletins, Conference Papers, UPM News, Newspaper Cuttings, Patents and Inaugural Lectures.

As the policy of the university does not permit users to view thesis in full text, access is only given to the first 24 pages only.