Thermal Diffusivity Measurement of Zinc‐Aluminum‐Layered Double Hydroxide using Photoflash Technique.

Ranjbar, Maryam and Mat Yunus, Wan Mahmood and Hussein, Mohd. Zobir and A. Moksin, Mohd Maarof and Haydari, Mehdi (2007) Thermal Diffusivity Measurement of Zinc‐Aluminum‐Layered Double Hydroxide using Photoflash Technique. AIP Conference Proceedings, 1017 . pp. 417-721. ISSN 0094-243X (print) , 0094-243X (online)

Full text not available from this repository.

Abstract

The photoflash technique has been widely used for measuring thermal diffusivity of various types of materials. In this report thermal diffusivity of Zn‐Al layered double hydroxide synthesized at different ratios of Zn to Al composition is presented. The samples were prepared using Zn(NO3)2 and Al(NO3)3 solutions at pH of 10 by drop wise addition of NaOH solution with vigorous stirring under nitrogen atmosphere. Different compositions of Zn to Al molar ratios were obtained by changing the molar ratio of Zn(NO3)2 to Al(NO3)3. The slurry formed was kept at 70 °C in an oil bath shaker for 18 h, filtered, washed and dried in an oven for 18 h at 70 °C. A simple photo flash and polyvinlidene diflouride (PVDF) film was used as light source and thermal wave detector, respectively. Thermal diffusivity of Zn‐Al layered double hydroxide measure at room temperature was found increase with different compositions for Zn‐Al ratio of 3–5.

Item Type:Article
Keyword:Thermal diffusivity; photoflash; Double Hydroxide.
Subject:Thermal diffusivity.
Faculty or Institute:Faculty of Science
Publisher:AIP American Institute of Physics
DOI Number:http://link.aip.org/link/doi/10.1063/1.2940673
ID Code:17390
Deposited By: Najwani Amir Sariffudin
Deposited On:15 May 2012 01:18
Last Modified:15 May 2012 01:18

Repository Staff Only: item control page

Document Download Statistics

This item has been downloaded for since 15 May 2012 01:18.

View statistics for "Thermal Diffusivity Measurement of Zinc‐Aluminum‐Layered Double Hydroxide using Photoflash Technique."


Universiti Putra Malaysia Institutional Repository

Universiti Putra Malaysia Institutional Repository is an on-line digital archive that serves as a central collection and storage of scientific information and research at the Universiti Putra Malaysia.

Currently, the collections deposited in the IR consists of Master and PhD theses, Master and PhD Project Report, Journal Articles, Journal Bulletins, Conference Papers, UPM News, Newspaper Cuttings, Patents and Inaugural Lectures.

As the policy of the university does not permit users to view thesis in full text, access is only given to the first 24 pages only.