The effect of milling time on Ni0.5Zn0.5Fe2O4 compositional evolution and particle size distribution
Ismail, Ismayadi and Hashim, Mansor and Matori, Khamirul Amin and Alias, Rosidah (2009) The effect of milling time on Ni0.5Zn0.5Fe2O4 compositional evolution and particle size distribution. American Journal of Applied Sciences, 6 (8). pp. 1548-1552. ISSN 1546-9239
Full text not available from this repository.
Official URL: http://thescipub.com/pdf/10.3844/ajassp.2009.1548....
Problem statement: This study involved an investigation to ascertain the diffusion of NiO and ZnO into the tetrahedral and octahedral sites using mechanical alloying method. The effect of mechanical alloying towards particle size was also reported. Approach: NiO, ZnO and Fe2O3 precursors were mechanically alloyed to synthesis ultrafine powders of Ni0.5Zn0.5Fe2O4. Various milling times were employed to study the effect of milling time on the materials. The ultrafine powder was sampled after each milling time and further characterized using XRD to investigate the phases of the powder and the crystallite size, SEM for the morphology and TEM for particle size investigation. Results: The XRD spectra indicated the precursors reacted during milling with the diffusion of ZnO and followed by NiO into their respective crystallographic sites. SEM micrographs showed the agglomeration of powders due to high energy milling and TEM images proved the particles of the materials were of nanosize. Conclusion: It was concluded that samples prepared using mechanical alloying technique appear to be a potential method for large production due to the possible reduction of cost and also reduction of particle size against milling time.
|Keyword:||Mechanical alloying; NiZn ferrites; Milling.|
|Faculty or Institute:||Faculty of Science|
|Deposited By:||Najwani Amir Sariffudin|
|Deposited On:||18 Jul 2012 08:25|
|Last Modified:||18 Jul 2012 08:25|
Repository Staff Only: Edit item detail
Document Download Statistics
This item has been downloaded for since 18 Jul 2012 08:25.