Synthesis and charaterization of Magnesium Zinc Ferrites as electromagnetic source

Yahya, Noorhana and Mohamad Nor Aripin, Ami Salwani and A. Aziz, Azizuddin and Daud, Hanita and Mohd Zaid, Hasnah and Lim, Kean Pah and Maarof, Norehan (2008) Synthesis and charaterization of Magnesium Zinc Ferrites as electromagnetic source. American Journal of Engineering and Applied Sciences, 1 (1). pp. 54-57. ISSN 1941-7020

Full text not available from this repository.

Abstract

Fabrication of Mg1-XZnXFe2O4 (where x = 0.2, 0.3, 0.4 and 0.5) samples using a conventional technique is reported. Oxides of magnesium, zinc and iron with purity of about 99.99% were mixed with distilled water in a milling machine for 12 hours. They were then filtered and presintered at 1250°C and sintered at 1350°C for 10 h in air. The phase and the crystal structure of the asprepared samples were identified using X-Ray Diffraction analysis (XRD). Hysteresis graph was evaluated using Vibrating Sample Magnetometer (VSM) to get the saturation magnetization (emu g-1)and coercivity (G) value. Atomic Force Microscope (AFM) was used to observe the surface morphology. The X-ray diffraction analysis showed major peak at plane (3 1 1) of the cubic structure for all the ferrites. The largest value of density achieved was 4.69 gcm-3 which was exhibited by sample with 0.5 mole fraction of zinc content. Highest saturation magnetization value (3.652emu g-1)was obtained for the 0.3 mole fraction of zinc content. A strong correlation between the saturation magnetization and zinc content was observed. We speculate that it is due to the Heisenberg superexchange interaction of magnetic Fe3+ and non-magnetic Zn2+ occupying the tetrahedral sites. The sample was used to induce electromagnetic (EM) waves in high operating frequency (5 MHz).

Item Type:Article
Keyword:Tetrahedron; X-ray diffraction; Hysteresis; Electromagnetic field; Super-exchange interaction
Subject:Ferrites - Analysis
Subject:X-rays - Diffraction
Subject:Electromagnetic fields
Faculty or Institute:Faculty of Science
Publisher:Science Publications
ID Code:16938
Deposited By: Najwani Amir Sariffudin
Deposited On:27 Aug 2012 09:20
Last Modified:27 Aug 2012 09:20

Repository Staff Only: item control page

Document Download Statistics

This item has been downloaded for since 27 Aug 2012 09:20.

View statistics for "Synthesis and charaterization of Magnesium Zinc Ferrites as electromagnetic source"


Universiti Putra Malaysia Institutional Repository

Universiti Putra Malaysia Institutional Repository is an on-line digital archive that serves as a central collection and storage of scientific information and research at the Universiti Putra Malaysia.

Currently, the collections deposited in the IR consists of Master and PhD theses, Master and PhD Project Report, Journal Articles, Journal Bulletins, Conference Papers, UPM News, Newspaper Cuttings, Patents and Inaugural Lectures.

As the policy of the university does not permit users to view thesis in full text, access is only given to the first 24 pages only.