Hussein, Mohd. Zobir and Bahar, F.A. and Yahya, Asmah (2010) Synthesis and characterization of hippurate-layered double hydroxide nanohybrid and investigation of its release property. Journal of the Iranian Chemical Society, 7 . S42-S51. ISSN 1735-207X
Full text not available from this repository.
Official URL: http://www.sid.ir/en/VEWSSID/J_pdf/8832010S04.pdf
The anion of hippuric acid, hippurate (A-), as an organic guest was intercalated into the interlayers of anionic clay, Zn/Al hydrotalcite-like or layered double hydroxides (LDH) host by direct co-precipitation method from aqueous solution for the formation of new nanohybrid compounds, Zn/Al-hippurate nanohybrids (ZAHs). Various Zn/Al molar ratios (R) = 3-5 and concentrations of HA (0.06-0.15 M) were used for the synthesis. ZAHs synthesized, using 0.15 M HA, was found to give wellordered layered nanohybrid materials with an increase of the basal spacing to 19.6-21.0 Å compared to 8.8-9.0 Å in the LDHs. The increase in the basal spacing is due to the insertion of A- organic moiety into the LDH interlayers. Formation of the host-guest type of material was confirmed by XRD, FTIR, TGA/DTG and compositional analysis. The release of the intercalated guest was found to be tunable in a controlled manner by Zn/Al molar ratio and is governed by pseudo-second order kinetics. Thus, by varying the experimental conditions, the release property of the guest anion can be tailored as required.
|Keyword:||Anionic clay; Hippuric acid; Intercalation; Layered double hydroxides; Hydrotalcite; Nanohybrid|
|Subject:||Layered double hydroxides|
|Faculty or Institute:||Faculty of Science|
|Publisher:||Iranian Chemical Society|
|Deposited By:||Najwani Amir Sariffudin|
|Deposited On:||28 Nov 2012 09:03|
|Last Modified:||28 Nov 2012 09:03|
Repository Staff Only: item control page
Document Download Statistics
This item has been downloaded for since 28 Nov 2012 09:03.