Study of thermal diffusivity of Zn/Al layered double hydroxide synthesized with different molar ratio of Zn/Al salts


Citation

Ranjbar, Maryam and Shameli, Kamyar and Ahmad @ Ayob, Mansor and Mat Yunus, Wan Mahmood and Hussein, Mohd Zobir and Shameli, Kaveh (2014) Study of thermal diffusivity of Zn/Al layered double hydroxide synthesized with different molar ratio of Zn/Al salts. Digest Journal of Nanomaterials and Biostructures, 9 (2). pp. 585-592. ISSN 1842-3582

Abstract

Thermal diffusivity of zinc-aluminum layered double hydroxides synthesized at different molar ratios of Zn to Al; at pH 7, 8 and 10 were measured using polyvinlidene diflouride (PVDF) photoflash technique. The samples were prepared using Zn (NO3)2 and Al (NO3)3 solutions by dropwise addition of NaOH solution with vigorous stirring under nitrogen atmosphere. The different ratios of Zn to Al were obtained by changing the molar ratio of Zn (NO3)2 to Al (NO3)3 solutions. The slurry formed was kept at 70 °C in an oil bath shaker for 18 h and then filtered, washed and dried in an oven for another 48 h at 70 °C. A simple photoflash and PVDF transducer were used as light source and thermal wave detector, respectively. All the measurements of thermal diffusivity of Zn-Al layered double hydroxide were carried out at room temperature. Thermal diffusivity for all series of sample prepared at pH=7, 8 and 10 increase from R=3 to R=5. Thermal diffusivity values of zinc-aluminum layered doubled hydroxide synthesized at pH 8 are higher than the values obtained for samples prepared at pH=7 (except for R=5) and at pH 10 are highest than two other series at pH 7 and 8.


Download File

[img]
Preview
Text (Abstract)
35512.pdf

Download (36kB) | Preview

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
Publisher: Institute of Materials Physics
Keywords: Thermal diffusivity; Zn-Al ratio; LDH; Photo - flash; Polyvinlidene diflourid
Depositing User: Nurul Ainie Mokhtar
Date Deposited: 11 Jan 2016 03:50
Last Modified: 11 Oct 2018 03:53
URI: http://psasir.upm.edu.my/id/eprint/35512
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item