Dielectric properties, impedance analysis and modulus behavior of CaTiO3 ceramic prepared by solid state reaction


Citation

Wong, Yick Jeng and Hassan, Jumiah and Hashim, Mansor (2013) Dielectric properties, impedance analysis and modulus behavior of CaTiO3 ceramic prepared by solid state reaction. Journal of Alloys and Compounds, 571. pp. 138-144. ISSN 0925-8388; ESSN:1873-4669

Abstract

Calcium titanate (CaTiO3) with the general formula for perovskites, ABO3, is of technological importance, particularly with regard to dielectric properties. In this work, CaTiO3 ceramic material was prepared by the conventional solid state reaction method. The dielectric properties, impedance characteristics and modulus behavior of the CaTiO3 ceramic material sintered at 1240 °C were investigated in the frequency range of 10−2–106 Hz and temperature range of 100–250 °C. The XRD analysis of the sintered CaTiO3 shows that it is an orthorhombic structure with lattice parameters a = 5.4398 Å, b = 7.6417 Å, and c = 5.3830 Å. The FESEM micrograph shows a significant difference in grain size distribution ranging from 0.26 to 2.32 μm. The AC conductivity, σAC, is found to increase with increasing temperature within the frequency range of 10−2–106 Hz confirming the hopping of electrons to be the conduction mechanism. Due to the decreasing values of the frequency exponent s with increasing temperature, the results of the σAC are discussed using the correlated barrier height (CBH) model. For dielectric studies, the dielectric constant, ε′ is found to decrease with increasing frequency. In the whole temperature range of 100–250 °C, high and low frequency plateau are observed. Each converges at high frequency (>105 Hz) for all the temperatures. The frequency dependence of loss tangent, tan δ, decreases with rise in temperature, with the loss tangent peak shifting to higher frequency. Due to its dielectric characteristics, it is a suitable candidate for developing a variety of capacitors. For the master modulus plot, the shapes remain unchanged in the temperature range considered. The Cole–Cole plots reveal that two primary relaxation processes exist in the sample for each temperature. The Nyquist plots reveal that at temperatures below 150 °C, a linear response in the imaginary part of the impedance, Z′′, is noticed. At and above 175 °C, the linear response gradually changes to a semicircle arc. The modulus behavior indicates the presence of correlation between the motions of mobile charge carriers. The plots of Arrhenius diagram of relaxation times of loss tangent, τtanδ, and imaginary part of dielectric modulus, τM′′, obey the Arrhenius law, where the activation energies calculated from the slopes are 2.09 and 2.38 eV respectively.


Download File

[img]
Preview
PDF (Abstract)
Dielectric properties impedance analysis and modulus behavior of CaTiO3 ceramic prepared by solid state reaction.pdf

Download (156kB) | Preview

Additional Metadata

Item Type: Article
Divisions: Faculty of Science
Institute of Advanced Technology
DOI Number: https://doi.org/10.1016/j.jallcom.2013.03.123
Publisher: Elsevier
Keywords: Dielectric response; Ceramics; Solid state reaction; Sintering.
Depositing User: Umikalthom Abdullah
Date Deposited: 20 Oct 2014 08:05
Last Modified: 09 Oct 2015 01:18
Altmetrics: http://www.altmetric.com/details.php?domain=psasir.upm.edu.my&doi=10.1016/j.jallcom.2013.03.123
URI: http://psasir.upm.edu.my/id/eprint/30278
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item